Unipreg® 80 g/sq m

Unipreg®Unipreg® - Fabric


TOW PROPERTIES:

  US Units (English) SI Units (Metric)
Tow
Zoltek Panex® 35 Continuous Tow
Tensile strength 600 Ksi 4137 MPa
Tensile modulus 35 Msi 242 GPa
Elongation 1.5 % 1.5 %
Density 0.065 lb/in3 1.81 g/cm3
Filament Diameter 0.283 mils 7.2 μm
Yield 400 ft/lb 270 m/kg

FABRIC PROPERTIES:

  US Units (English) SI Units (Metric)
Area weight 2.36 oz/yd2 (+0.06oz/yd2) 80 g/m2 (+ 2 g/m2)
Standard production width 19.69 in (± 0.1181 in) 500 mm (± 3 mm)
Maximum production width 23.62 in (± 0.1181 in) 600 mm (± 3 mm)
Laminate thickness 0.00315 in (± 2.5 %) 0.08 mm (± 2.5 %)
Bonding lay
(76 dtex polyester scrim on 1 or 2 sides to keep together the carbon structure)
0.10 oz/yd2 3.5 g/m2
Core diameter 11.81 in 300 mm
Core length 27.56 in
700 mm
Curing temperature 176 oF - 302 oF 80 oC - 150 oC
Tg 158 oF - 284 oF 70 oC - 140 oC
Resin system
Epoxy
Shelf life at ambient temperature (20 °C) 4 months
Shelf life at -18 °C 18 months

Typical properties of the composite laminate made from Unipreg®140:

Tensile Strength EN ISO 527-4
1800 MPa
Tensile Modulus
EN ISO 527-4
139 GPa
Flexural Strength EN ISO 14125
1670 MPa
Flexural Modulus EN ISO 14125
115 GPa
ILS Strength EN ISO 14130
73 MPa
Density
EN ISO 1183
1.57 g/cm3