Unipreg® 200 g/sq m

Unipreg® Unipreg® - Fabric

TOW PROPERTIES:

	US Units (English)	SI Units (Metric)
Tow	Zoltek Panex® 35 Continuous Tow
Tensile strength	600 Ksi	4137 MPa
Tensile modulus	35 Msi	242 GPa
Elongation	1.5 %	1.5 %
Density	0.065 lb/in³	1.81 g/cm³
Filament Diameter	0.283 mils	7.2 μm
Yield	400 ft/lb	270 m/kg

FABRIC PROPERTIES:

	US Units (English)	SI Units (Metric)
Area weight	5.90 oz/yd² (+0.06oz/yd²)	200 g/m² (+ 2 g/m²)
Standard production width	19.69 in (± 0.1181 in)	500 mm (± 3 mm)
Maximum production width	23.62 in (± 0.1181 in)	600 mm (± 3 mm)
Laminate thickness	0.007874 in (± 2.5 %)	0.20 mm (± 2.5 %)
Bonding lay (76 dtex polyester scrim on 1 or 2 sides to keep together the carbon structure)	0.10 oz/yd²	3.5 g/m²
Core diameter	11.81 in	300 mm
Core length	27.56 in	700 mm
Curing temperature	176 ^oF - 302 ^oF	80 ^oC - 150 ^oC
Tg	158 ^oF - 284 ^oF	70 ^oC - 140 ^oC
Resin system	Epoxy
Shelf life at ambient temperature (20 °C)	4 months
Shelf life at -18 °C	18 months

Typical properties of the composite laminate made from Unipreg^®140:

Tensile Strength	EN ISO 527-4	1800 MPa
Tensile Modulus	EN ISO 527-4	139 GPa
Flexural Strength	EN ISO 14125	1670 MPa
Flexural Modulus	EN ISO 14125	115 GPa
ILS Strength	EN ISO 14130	73 MPa
Density	EN ISO 1183	1.57 g/cm³

* This information is based on our present state of knowledge. UNICARBON^® cannot guarantee that the data listed above will be achieved with other processes.

TECHNICAL DATA SHEET