Unipreg® 30 g/sq m


TOW PROPERTIES:
|
US Units (English) |
SI Units (Metric)
|
Tow
|
Toray T700SC-12000 |
Tensile strength |
711 Ksi |
4900 MPa
|
Tensile modulus |
33.4 Msi |
230 GPa
|
Elongation |
2.1% |
2.1% |
Density |
0.065 lbs/in3 |
1.80 g/cm3 |
Filament Diameter |
2.8E-04 in |
7 μm |
Yield |
1,862 ft/lbs |
800 g/1000m |
FABRIC PROPERTIES:
|
US Units (English) |
SI Units (Metric)
|
Area weight |
0.88 oz/yd2 (+0.06oz/yd2) |
30 g/m2 (+ 2 g/m2)
|
Standard production width |
19.69 in (± 0.1181 in) |
500 mm (± 3 mm) |
Maximum production width |
23.62 in (± 0.1181 in) |
600 mm (± 3 mm) |
Laminate thickness |
0.001181 in (± 2.5 %) |
0.03 mm (± 2.5 %) |
Bonding lay (76 dtex polyester scrim on 1 or 2 sides to keep together the carbon structure) |
0.10 oz/yd2 |
3.5 g/m2 |
Core diameter |
11.81 in |
300 mm |
Core length |
27.56 in
|
700 mm |
Curing temperature |
176 oF - 302 oF |
80 oC - 150 oC |
Tg |
158 oF - 284 oF |
70 oC - 140 oC |
Resin system
|
Epoxy |
Shelf life at ambient temperature (20 °C) |
4 months |
Shelf life at -18 °C |
18 months |
* This information is based on our present state of knowledge. UNICARBON® cannot guarantee that the data listed above will be achieved with other processes.
TECHNICAL DATA SHEET